RESINA BICOMPONENTE EPOSSIDICA EPOSEALER SOL.A+SOL.B

IMPREGNATING EPOSEALER AND TWO-COMPONENT ANTIOSMOSIS A + B



€24.00

Epoxy resin for boat treatment

Qty

PayPal

EPOSEALER IMPREGNATION AND TWO-COMPONENT ANTIOSMOSIS A + B

It is a solvent-free liquid epoxy resin catalyzed with a cycloaliphatic amine with high insulating and adhesive power

Given its characteristics of penetration, adhesion, flexibility and water resistance, this resin is able to waterproof the wood while maintaining its original properties intact

It is therefore the most suitable product for the treatment and restoration of wood

This resin also has exceptional anti-osmosis properties and can be used for this problem on fiberglass boats

0.750lt pack

PREPARATION OF THE SUPPORT AND APPLICATION CYCLE
IMPREGNATION. Clean, degrease and sand the surfaces of the wood to be treated. Make sure that the wood is dry, apply 3-4 coats of EPOSEALER IMPREGNAZIONE E ANOSOSOSOSI at a distance of 12–24 hours from each other thus obtaining a final thickness of about 300 microns. Within 24 hours from the last coat of EPOSEALER IMPREGNATION AND ANTIOSMOSIS, apply one coat of our UNIFIBER PRIMER. EPOSEALER IMPREGNATION AND ANTI-OSMOSIS is applied by brush or roller.

OSMOSIS. For the treatment of the hulls affected by osmosis completely remove the layer of Gel Coat, eliminate (better by sandblasting) the osmosis bubbles with complete opening of the craters. Wash thoroughly with fresh water, preferably warm. Before treatment, make sure that the hull is perfectly dry. Apply on the osmosis areas 1 coat of EPOSEALER IMPREGNAZIONE E ANTIOSMOSI, after 12-24 hours apply a complete coat on the whole surface of the living work. Within 24 hours, smooth the osmosis craters with EPOXY LIGHT FILLER NS until obtaining, with several grouting and correspondence cycles, a completely smoothed surface (if necessary, use PLAMUR FINISHER putty for finishing. Subsequently apply 3-4 coats of EPOSEALER IMPREGNAZIONE E ANTIOSMOSIS (12-24 hours apart) to obtain a total thickness of 600 microns. Within 24 hours of the last coat, apply one coat of UNIFIBER PRIMER. EPOSEALER IMPREGNATION AND ANTIOSMOSIS is applied by brush or roller. L The recommended application is a short-haired roller that allows thicknesses of 100-120 microns per coat.

Type

Bicomponente
Type of binder sol a Liquid epoxy resin
Specific weight kg / lt (± 0.05) 1.130 (A) - 0.970 (B)
Viscosity ford 12 sec. (Ø8 at 20 ° C)
Storage (+ 10- + 30c) 12 months sealed containers

Application

Roller brush
Blend a + b by volume 2 parts of Sol.A with 1 of Sol.B
Pot life a + b (20c) Use mixture within 30-50 minutes
Brush-roller dilution Ready to use. As primer for new wood: 40-50% Thinner 765 (or Epowood)
Dust-free drying n, d,
Overpainting time 24 hours (20 ° c)
Application temperature Between +10 c and +40 c
Relative humidity Less than 80%
Dry thickness recommended 100 microns per coat
Theoretical yield m2 / liter 5
G4420000500
15 Items

Specific References

Review

Write your review

IMPREGNATING EPOSEALER AND TWO-COMPONENT ANTIOSMOSIS A + B

Epoxy resin for boat treatment

Write your review

Related Product